Intense white photoluminescence emission of V-implanted ZnO oxide thin films

Pulsed laser deposited ZnO films were imlpanted with vanadium ions using ion energies between 30 and 250 keV with different fluences yielding vanadium concentrations in the range between 0.8 and 5 at. %. After annealing under oxygen ambient at 800°C, a broad luminescence band observed by photoluminescence covers nearly the total visible spectral region. This luminescence is a superposition of different bands triggered by the incoporated V and remaining implantation defects. The visual impression of the bright whitish emission of the implanted ZnO has been quantified using the color space map of the Commission internationale de l'Eclairage. Furthermore, the intensity of the white emission strongly increases with increasing V concentration, whereas Ar-implanted reference sample shows only weak white emission.