Vibrations Analysis of Bubble Evolution in Liquids of Varying Physical Properties

In recent years there is an attempt to control the gas stirring intensity in metal-making ladles with the aid of vibration measurements. Understanding better the induced vibrations in two-phase flows can substantially improve the existing models for gas stirring control. In this work, highly sensitive accelerometers were used for the vibration measurements in a liquid metal alloy; Sn–40 wt pctBi alloy at 200 °C and water at 20 °C. The examination of the liquids was conducted in the ladle mockup integrated into the Liquid Metal Model for Steel Casting facility at Helmholtz-Zentrum Dresden Rossendorf. Single bubbles were generated in the respective
liquids by controlled argon injection at low flow rates in the range of 0.01 to 0.15 NL/min through a single nozzle installed at the bottom of the ladle. Obtained results demonstrate differences between the induced vibrations in the examined liquids in terms of the magnitude of the root mean square values of vibration amplitude and the shape of the resulting curves with increasing flow rate. Furthermore, continuous wavelet transform reveals variations in the duration and vibrational frequency of the evolved bubble phenomena. The findings suggest that
differences in the physical properties of the examined liquids result in variations in the vibrations induced during bubble evolution.